T-HR 2320

T-HR 2320 is a styrenic terpolymer (ABS) grade with improved toughness versus HIPS grades. It exhibits low shrinkage and good dimensional stability. T-HR 2320 is used in general injection molding applications, particularly for furniture, automotive parts, general injection molding, appliance casings, and home appliances with heat resistance characteristics.

Category:

Description

Product Name: T-HR 2320

Description:
T-HR 2320 is a styrenic terpolymer (ABS) grade with improved toughness versus HIPS grades. It exhibits low shrinkage and good dimensional stability. T-HR 2320 is used in general injection molding applications, particularly for furniture, automotive parts, general injection molding, appliance casings, and home appliances with heat resistance characteristics.

Drying Instructions:
Drying before processing is recommended in a desiccant dehumidifying hopper dryer. An inlet air dew point of -20°F (-29°C) or below is suggested to reach 0.1% moisture content. Typical drying conditions are 2 hours at 180°-190°F (82°-88°C) or 4 hours at 160°-170°F (71°-77°C).

Physical and Mechanical Properties:

Property Unit Test Method Typical Value
Melt Flow Index (200°C/5KG) GR/10MIN ASTM D-1238 1.2
Izod Impact Strength KGf.CM/CM ASTM D-256 20
Vicat Softening Point (5KGF LOAD) °C ASTM D-1525 103
Tensile Strength at Yield KGf/CM2 ASTM D-638 470
Elongation at Break % ASTM D-638 12
Tensile Modulus KGf/CM2 ASTM D-638 20000
Rockwell Hardness (at 23°C) R.SCALE ASTM D-785 107

Additional InformationAll above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests. For more information about guaranteed items, please refer to S.S.S. (Standard Sales Specifications).

 