Description
Product Name: T-HIPS 8350
Product Description: T-HIPS 8350 is a high-impact polystyrene designed for extrusion sheets, offering improved ESCR compared to other high-impact polystyrene types like HIPS 7240. It provides excellent melt strength, making it ideal for deep-draw thermoforming. T-HIPS 8350 is suited for packaging applications that may involve stress cracking from fats, oils, or low temperatures, including products requiring contact with HCFC-expanded foam insulation.
Applications:
- Thermoforming
- Fridge doors and cabinet liners
- Packaging for fatty food sheets
Physical and Mechanical Properties:
Property | Unit | Test Method | Typical Value |
---|---|---|---|
MELT FLOW INDEX (200°C 5KG) | g/10min | ASTM D-1238 | 4.5 |
STYRENE RESIDUAL MONOMER | PPM | ATOFINA Test | <500 |
VICAT SOFTENING POINT (50 °C/hr 1kg) | °C | ASTM D-1525 | 96 |
ROCKWELL HARDNESS | – | ASTM D-785 | SCALE/R54 |
TENSILE STRESS AT YIELD | MPA | ASTM D-638 | 18 |
TENSILE STRENGTH AT BREAK | MPA | ASTM D-638 | 20 |
ELONGATION AT BREAK | % | ASTM D-638 | 60 |
TENSILE MODULUS | MPA | ASTM D-638 | 1600 |
IZOD IMPACT | KJ/M2 | ASTM D-256 | 13 |
Additional Notes:
- All values are typical and should not be construed as specifications. Users are advised to confirm through their own tests.
- Density and shrinkage values of this grade are approximately 1.04 kg/lit and (0.4-0.7)% as per ASTM D-955.
- Tests are conducted at 23°C unless specified otherwise.