T-HIPS 7240

T-HIPS 7240 is a very high-impact polystyrene for the extrusion industry. This grade has been designed to be diluted with crystal polystyrene. The good melt strength of this grade makes it particularly suited for deep-draw thermoforming.

Category:

Description

ProductT-HIPS 7240

Description: T-HIPS 7240 is a very high-impact polystyrene for the extrusion industry. This grade has been designed to be diluted with crystal polystyrene. The good melt strength of this grade makes it particularly suited for deep-draw thermoforming. T-HIPS 7240 is available in white color.

Applications:

  • Dairy sheet, cups, trays, egg boxes, general packaging, coextrusion with GPPS at industrial sheets.

Physical and Mechanical Properties

Property Unit Test Method Typical Value
Melt Flow Index (200°C 5KG) g/10min ASTM D-1238 4.5
Styrene Residual Monomer PPM CLG LABPSG004 (ATOFINA TEST METHOD) <500
Vicat Softening Point (50 °C/hr 1kg) °C ASTM D-1525 97
Rockwell Hardness ASTM D-785 SCALE/R65
Tensile Stress at Yield MPA ASTM D-638 23
Tensile Strength at Break MPA ASTM D-638 21
Elongation at Break % ASTM D-638 60
Tensile Modulus MPA ASTM D-638 1950
Izod Impact KJ/M2 ASTM D-256 11

Additional Notes:

  • All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests. For more information about guaranteed items, please refer to S.S.S. (Standard Sales Specifications).
  • Density and shrinkage of this grade are approximately around 1.04 kg/lt & (0.4-0.7) % (ASTM D-955) respectively.
  • All tests are carried out at 23°C, unless otherwise stated.
  • If in grade reference the fourth digit is “1” (7241), it indicates an external lubricant is included.