T-GPPS 1460

GPPS 1460 is a high heat resistance and molecular weight crystal polystyrene designed for extrusion and thick-walled injection molding applications. It’s especially suitable for thick sheet production by direct inject gassing, providing expanded sheets with high mechanical properties.

Category:

Description

ProductT-GPPS 1460

Description: GPPS 1460 is a high heat resistance and molecular weight crystal polystyrene designed for extrusion and thick-walled injection molding applications. It’s especially suitable for thick sheet production by direct inject gassing, providing expanded sheets with high mechanical properties.

Applications: Insulation board (XPS), foam sheets for food & fruit trays.


Physical and Mechanical Properties:

Property Unit Test Method Typical Value
MELT FLOW INDEX (200°C 5KG) g/10min ASTM D-1238 6.5
STYRENE RESIDUAL MONOMER PPM CLG LABPSG004 (ATOFINA TEST METHOD) <500
VICAT SOFTENING POINT (50°C/hr 1kg) °C ASTM D-1525 103
TENSILE STRENGTH AT BREAK MPA ASTM D-638 48
ELONGATION AT BREAK % ASTM D-638 1
TENSILE MODULUS MPA ASTM D-638 3200

Additional Notes:

  • All mentioned data are typical values and not to be construed as real specifications. Users should confirm results through their tests. For more information about guaranteed items, please refer to S.S.S. (Standard Sales Specifications).
  • Density and shrinkage of this grade are approximately around 1.04 kg/lit & (0.4-0.7)% (ASTM D-955) respectively.
  • All tests are carried out at 23°C, unless otherwise specified.
  • If the injection molding products quality is affected by moisture, GPPS granules can be dried at 70°C for 2-4 hours.

 