MDPE S403313

MDPE S403313 is a medium-density polyethylene with a broad molecular weight distribution and high melt strength. Produced using 1-hexene as a comonomer, it is specially designed for thin films requiring high tear resistance, good sealability, high strength, and high drawdown. It is suitable for manufacturing high-strength carrier bags and high-quality thin films for uni/multi-wall packaging.

Category:

Description

MDPE S403313 is a medium-density polyethylene with a broad molecular weight distribution and high melt strength. Produced using 1-hexene as a comonomer, it is specially designed for thin films requiring high tear resistance, good sealability, high strength, and high drawdown. It is suitable for manufacturing high-strength carrier bags and high-quality thin films for uni/multi-wall packaging.

General Information:

  • Status: Commercial: Active
  • Application: Blown film extrusion, Uni/multi-wall packaging, High-quality thin films, High-strength carrier bags
  • Form(s): Pellet

Attributes:

  • High melt stability
  • Very good tear resistance
  • High strength and toughness
  • Good sealability

Additives:

  • Antioxidant: Yes
  • Processing Aid: No
  • Antiblock: No
  • Slip Agent: No

 

Property Typical Value Unit Test Method
Physical
High Load Melt Flow Index (190°C/21.6 kg) 13 g/10 min ISO 1133
Density 0.933 g/cm³ ISO 1183
Mechanical
Tensile Modulus of Elasticity 620 MPa ISO 527-1,2
Tensile Strength (MD) 55 MPa ISO 527-1,3
Tensile Strength (TD) 43 MPa ISO 527-1,3
Tensile Strain at Break (MD) 600 % ISO 527-1,3
Tensile Strain at Break (TD) 600 % ISO 527-1,3
Elmendorf Tear Strength (MD) 330 mN ISO 6383-2
Elmendorf Tear Strength (TD) 2000 mN ISO 6383-2
Failure Energy 8.5 J/mm DIN 53373
Dart Drop Impact 160 g ASTM D1709
Thermal
Melting Temperature 124 °C ISO 3146
Vicat Softening Temperature (10N) 116 °C ISO 306

Recommended Process Conditions:

  • Extruder Temperature Profile: 190-235°C
  • Blow-Up Ratio: 3-5
  • Film Thickness: 10-50 μm