Description
LDPE S202185 is a high molecular weight, low-density polyethylene with good toughness and excellent biaxial shrink properties. This product contains no slip or antiblock additives and offers good melt strength and drawdown ability during processing.
General Information:
- Status: Commercial: Active
- Application: Blown film extrusion, Thin packaging films and bags, Thin shrink films
- Form(s): Pellet
Attributes:
- Very suitable for producing thin shrink films
- Good toughness and biaxial properties
Additives:
- Antioxidant: Yes
- Antiblock: No
- Slip Agent: No
| Property | Typical Value | Unit | Test Method |
|---|---|---|---|
| Physical | |||
| MFI (190°C/2.16 Kg) | 0.85 | dg/min | ISO 1133 |
| Density | 921 | kg/m³ | ISO 1183 (A) |
| Mechanical | |||
| Impact Strength | 28 | kJ/m | ASTM D4272 |
| Tear Strength (TD) | 30 | kN/m | ISO 6383-2 |
| Tear Strength (MD) | 40 | kN/m | ISO 6383-2 |
| Yield Stress (TD) | 11 | MPa | ISO 527-1,3 |
| Yield Stress (MD) | 12 | MPa | ISO 527-1,3 |
| Tensile Stress at Break (TD) | 21 | MPa | ISO 527-1,3 |
| Tensile Stress at Break (MD) | 24 | MPa | ISO 527-1,3 |
| Strain at Break (TD) | > 500 | % | ISO 527-1,3 |
| Strain at Break (MD) | > 200 | % | ISO 527-1,3 |
| Modulus of Elasticity (TD) | 170 | MPa | ISO 527-1,3 |
| Modulus of Elasticity (MD) | 160 | MPa | ISO 527-1,3 |
| Optical | |||
| Haze | 9 | % | ASTM D1003 A |
| Gloss (45°) | 60 | GU | ASTM D2457 |
| Clarity | 27 | mV | SABTEC method |
Recommended Process Conditions:
- Extruder Temperature Profile: 175-190 °C
- Blow-Up Ratio: 2-4
- Film Thickness: 45-100 μm