Description
Product Name: ILHD 107000F
Description:
ILHD 107000F is a high molecular weight, high-density polyethylene copolymer with a broad molecular weight distribution. The product’s molecular architecture and density provide a unique combination of easy extrusion and high melt strength with strong physical properties, making it suitable for producing thin films with excellent strength and rigidity.
Typical Applications:
ILHD 107000F is recommended for blown film extrusion. It is ideal for manufacturing high-strength grocery sacks, shopping bags, and high-quality thin films for multi-wall sack liners and replacements for thin paper products. Films produced with this product can be easily treated and printed for high-quality graphics.
Typical Property Values
| Properties | Typical Values | Units | Test Methods |
|---|---|---|---|
| Polymer Properties | |||
| Melt Flow Rate (MFR) at 190°C, 5 kg load | 0.04 | g/10 min | ISO 1133 |
| Density at 23°C | 952 | kg/m³ | ISO 1183 |
| Mechanical Properties | |||
| Tensile Stress at Yield | 27 | MPa | ISO 527-1/-2 |
| Tensile Stress at Break | >24 | MPa | ISO 527-1/-2 |
| Elongation at Break | >500 | % | ISO 527-1/-2 |
| Charpy Impact Strength | NB | kJ/m² | ISO 179-1 |
| Shore Hardness | 64 | D scale | ISO 868 |
| Stress Cracking Resistance | >600 | Hr | ASTM 1693 |
| Vicat Softening Temperature | 131 | °C | ISO 11357 |
| Melting Temperature | 124 | °C | ISO 306 |
- Typical values; not to be construed as specification limits.
- Based on compression molded sheets. Test specimens are conditioned at 23 °C and 50% relative humidity for 24 hours.
Processing Conditions
- Melt Temperature: 200 – 215°C
- Frost Line Height: 6-8 times the die diameter
Storage and Handling
Polyethylene material should be stored to avoid direct sunlight and heat exposure. The storage area should be dry and kept below 50°C. Poor storage conditions may lead to quality deterioration such as color change, bad smell, and inadequate performance.
Packaging
Available in 25 kg bags or 1375 kg shrink film palletized units.