A 203026H

A 203026H is an additivated, low-density polyethylene with high rigidity. It contains slip and anti-blocking agent. It is delivered in pellet form.

Categories: ,

Description

A 203026H is an additivated, low-density polyethylene with high rigidity. It contains slip and anti-blocking agent. It is delivered in pellet form.

Applications:

  • Cast & Blown Film
  • Bags & Pouches
  • Film & Shrink Film
  • Food Packaging Film
  • Surface Protection Film

Processing Method:

  • Cast Film
  • Blown Film

Features:

  • Opticals
  • Good Processability
  • Unspecified Slip
  • Low Friction
  • Good Stiffness

Technical Data Table:

A 203026H is an additivated, low-density polyethylene with high rigidity. It contains slip and anti-blocking agent. It is delivered in pellet form.

Applications:

  • Cast & Blown Film
  • Bags & Pouches
  • Film & Shrink Film
  • Food Packaging Film
  • Surface Protection Film

Processing Method:

  • Cast Film
  • Blown Film

Features:

  • Opticals
  • Good Processability
  • Unspecified Slip
  • Low Friction
  • Good Stiffness

Technical Data Table:

No. Property Value Units Test Method
1 Density 0.927 g/cm³ ISO 1183
2 Melt Flow Rate (MFR) (190°C/2.16Kg) 2.0 g/10 min ISO 1133
3 Tensile Modulus 300 MPa ISO 527-1, -2
4 Tensile Stress at Yield 13.0 MPa ISO 527-1, -2
5 Tensile Strength MD/TD 25/18 MPa ISO 527-1, -3
6 Tensile Strain at Break MD/TD 350/600 % ISO 527-1, -3
7 Dart Drop Impact (50 µm blown film) 110 g ASTM D 1709
8 Vicat Softening Temp (A50 (50°C/h 10N)) 100 °C ISO 306
9 Haze (50) <7.0 % ASTM D 1003
10 Gloss (60°, 50) >110 % ASTM D 2457

 