J-10CRP100 N (PE100) is a HDPE grade intended for applications including Grade: J-10CRP100 N (PE100); Density: 0.946 – 0.950 g/cm³. Review the listed technical properties and confirm current specifications, regulatory suitability and availability with the relevant supplier before purchase.
Representative disclosure:
Applications
- Grade: J-10CRP100 N (PE100)
- Density: 0.946 – 0.950 g/cm³
- Melt Flow Rate (MFR): 0.19 – 0.25 g/10 min (190°C/5 kg)
- Top-quality PE100 pressure pipes
- Pipes for gas and water transportation at higher pressure or with thinner walls than PE80 (UV stabilization and/or pigments during processing)
- Antioxidant / Process stabilizer
- Lubricant (processing aid) / Acid scavenger
- Material Properties: These data are typical values and should not be construed as actual product specifications. Users should conduct their own tests to confirm these properties.
- Testing Conditions: Test specimens are taken from compression molded sheets at 23°C. FRR values are statistical and calculated by dividing MFR values. Notch Impact Test specimen from compressed molded sheet at 23°C; the data quoted are average values.
- Test specimens are taken from compression molded sheets at 23°C.
- FRR values are statistical and calculated by dividing MFR values.
- Notch Impact Test specimen from compressed molded sheet at 23°C; the data quoted are average values.
Technical properties
Technical values are source-captured and pending confirmation against current supplier documentation.
| Test/Composition | Density | Typical Value | 0.948 | Unit | g/m³ | ASTM Method | ISO1183 |
|---|---|---|---|---|---|---|---|
| Test/Composition | FRR 21.6/5 | Typical Value | 28 | Unit | – | ASTM Method | – |
| Test/Composition | Hydrostatic Strength (80°C) | Typical Value | 5000 (4.5N/mm²) | Unit | h | ASTM Method | ISO1167 |
| Test/Composition | MFR190°/21.6 | Typical Value | 6.2 | Unit | g/10 min | ASTM Method | ISO1133 |
| Test/Composition | MFR190°/5 | Typical Value | 0.22 | Unit | g/10 min | ASTM Method | ISO1133 |
| Test/Composition | Notched Impact @ 23°C | Typical Value | 24 | Unit | mJ/mm² | ASTM Method | ISO179/1eA |