T-HIPS 7240 is a HIPS grade intended for applications including Dairy sheet, cups, trays, egg boxes, general packaging, coextrusion with GPPS at industrial sheets.; All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests. For more information about guaranteed items, please refer to S.S.S. (Standard Sales Specifications).. Review the listed technical properties and confirm current specifications, regulatory suitability and availability with the relevant supplier before purchase.
Representative disclosure:
Applications
- Dairy sheet, cups, trays, egg boxes, general packaging, coextrusion with GPPS at industrial sheets.
- All above mentioned data are typical values and not to be construed as real specifications. Users should confirm results by their own tests. For more information about guaranteed items, please refer to S.S.S. (Standard Sales Specifications).
- Density and shrinkage of this grade are approximately around 1.04 kg/lt & (0.4-0.7) % (ASTM D-955) respectively.
- All tests are carried out at 23°C, unless otherwise stated.
- If in grade reference the fourth digit is “1” (7241), it indicates an external lubricant is included.
Technical properties
Technical values are source-captured and pending confirmation against current supplier documentation.
| Property | Melt Flow Index (200°C 5KG) | Unit | g/10min | Test Method | ASTM D-1238 | Typical Value | 4.5 |
|---|---|---|---|---|---|---|---|
| Property | Styrene Residual Monomer | Unit | PPM | Test Method | CLG LABPSG004 (ATOFINA TEST METHOD) | Typical Value | <500 |
| Property | Vicat Softening Point (50 °C/hr 1kg) | Unit | °C | Test Method | ASTM D-1525 | Typical Value | 97 |
| Property | Rockwell Hardness | Unit | – | Test Method | ASTM D-785 | Typical Value | SCALE/R65 |
| Property | Tensile Stress at Yield | Unit | MPA | Test Method | ASTM D-638 | Typical Value | 23 |
| Property | Tensile Strength at Break | Unit | MPA | Test Method | ASTM D-638 | Typical Value | 21 |
| Property | Elongation at Break | Unit | % | Test Method | ASTM D-638 | Typical Value | 60 |
| Property | Tensile Modulus | Unit | MPA | Test Method | ASTM D-638 | Typical Value | 1950 |
| Property | Izod Impact | Unit | KJ/M2 | Test Method | ASTM D-256 | Typical Value | 11 |