J-109450F (EX5) is a HDPE grade intended for applications including Grade: J-109450F (EX5); Density: 0.947 – 0.951 g/cm³. Review the listed technical properties and confirm current specifications, regulatory suitability and availability with the relevant supplier before purchase.
Representative disclosure:
Applications
- Grade: J-109450F (EX5)
- Density: 0.947 – 0.951 g/cm³
- Melt Flow Rate (MFR): 0.23 – 0.33 g/10 min (190°C/5 kg)
- Blown films with pepper-like quality
- Suitable for counter bags, carrier bags, and wrapping films
- Excellent processing quality
- Antioxidant / Process stabilizer
- Lubricant (processing aid) / Acid scavenger
- Material Properties: These data are typical values and should not be construed as actual product specifications. Users should conduct their own tests to confirm these properties.
- Applications: This grade is designed for high molar mass film applications where good stiffness and tenacity are required.
- Testing Conditions: Test specimens are taken from compression molded sheets at 23°C. FRR values are statistical and calculated by dividing MFR values. Notch Impact Test specimen from compressed molded sheet at 23°C; the data quoted are average values.
- Test specimens are taken from compression molded sheets at 23°C.
- FRR values are statistical and calculated by dividing MFR values.
- Notch Impact Test specimen from compressed molded sheet at 23°C; the data quoted are average values.
Technical properties
Technical values are source-captured and pending confirmation against current supplier documentation.
| Test/Composition | Density | Typical Value | 0.949 | Unit | g/cm³ | Method | ISO1183 |
|---|---|---|---|---|---|---|---|
| Test/Composition | Fish Eye Note | Typical Value | ≤3 | Unit | note | Method | Internal |
| Test/Composition | FRR 21.6/5 | Typical Value | 29 | Unit | – | Method | – |
| Test/Composition | MFR 190°/21.6 | Typical Value | 8.0 | Unit | g/10min | Method | ISO1133 |
| Test/Composition | MFR190°/5 | Typical Value | 0.28 | Unit | g/10min | Method | ISO1133 |