HDPE S4265 is a HDPE grade intended for applications including Status: Commercial: Active; Application: Intermediate Bulk Container (IBC), Large Agricultural Tank, Small to Large Jerry Cans. Review the listed technical properties and confirm current specifications, regulatory suitability and availability with the relevant supplier before purchase.
Representative disclosure:
Applications
- Status: Commercial: Active
- Application: Intermediate Bulk Container (IBC), Large Agricultural Tank, Small to Large Jerry Cans
- Form(s): Pellet
- Very Good ESCR
- High Impact Resistance
- Very Good Creep Strength
- Easy Processability
- Good Chemical Resistance
- Antioxidant: Yes
- Processing Aid: No
- Antiblock: No
- Slip Agent: No
- Extruder Barrel Temperature: 200-230 °C
- Melt Temperature: 205-235 °C
Technical properties
Technical values are source-captured and pending confirmation against current supplier documentation.
| Property | Physical | Typical Value | Unit | Test Method | |||
|---|---|---|---|---|---|---|---|
| Property | High Load Melt Flow Index (190°C/21.6 kg) | Typical Value | 6.5 | Unit | g/10 min | Test Method | ISO 1133 |
| Property | Density | Typical Value | 0.942 | Unit | g/cm³ | Test Method | ISO 1183 |
| Property | Bulk Density | Typical Value | > 0.50 | Unit | g/cm³ | Test Method | ISO 60 |
| Property | Mechanical | Typical Value | Unit | Test Method | |||
| Property | Tensile Strength at Yield | Typical Value | 24 | Unit | MPa | Test Method | ISO 527-1, -2 |
| Property | Elongation at Yield | Typical Value | 10 | Unit | % | Test Method | ISO 527-1, -2 |
| Property | Tensile Modulus of Elasticity | Typical Value | 800 | Unit | MPa | Test Method | ISO 527-1, -2 |
| Property | FNCT (3.5 MPa, 2% Arkopal N100, 80°C) | Typical Value | 60 | Unit | hr | Test Method | ISO 16770 |
| Property | Impact | Typical Value | Unit | Test Method | |||
| Property | Tensile Impact Strength (Notched, -30°C) | Typical Value | 160 | Unit | kJ/m² | Test Method | ISO 8256 |
| Property | Thermal | Typical Value | Unit | Test Method | |||
| Property | Melting Temperature | Typical Value | 130 | Unit | °C | Test Method | ISO 3146 |
| Property | Vicat Softening Temperature (10N) | Typical Value | 128 | Unit | °C | Test Method | ISO 306 |
| Property | Deflection Temperature Under Load (0.45 MPa) | Typical Value | 70 | Unit | °C | Test Method | ISO 75 |
| Property | Deflection Temperature Under Load (1.8 MPa) | Typical Value | 52 | Unit | °C | Test Method | ISO 75 |